Copper Clad Aluminum Flat Wire
Copper Clad Aluminum Flat Wire features good conductivity and lightweight properties, suitable for motor windings, transformers, and inductors requiring efficient heat dissipation.
Specifications
| Material | Copper Clad Aluminum (Cu/Al) |
| Conductivity | 65% IACS |
| Tensile Strength | 170 MPa |
| Diameter | Width: 0.5mm-25mm, Thickness: 0.1mm-5mm |
Applications
Motor Windings Transformers Inductors Flat Cables
Manufacturing Process
This product is manufactured using Clad & Weld process with metallurgical bonding. It is NOT electroplated.
Detailed Specs
| Copper Content | 10-20% |
| Standards | ASTM B566, GB/T 23309 |
| Temper | Soft, Hard |
| R-angle Precision | ±0.01mm |
Frequently Asked Questions
Related Products
🏭
Copper Clad Aluminum Round Wire
Copper Clad Aluminum (Cu/Al)
Conductivity: 65% IACS
Diameter: 0.05mm - 12.0mm
🏭
Copper Clad Aluminum Strip
Copper Clad Aluminum (Cu/Al)
Conductivity: 65% IACS
Diameter: Width: 5mm-1000mm, Thickness: 0.1mm-5mm
🏭
Copper Clad Aluminum Foil
Copper Clad Aluminum (Cu/Al)
Conductivity: 65% IACS
Diameter: Thickness: 0.01mm-0.1mm, Width: 5mm-1000mm
🏭
Copper Clad Aluminum Ribbon Wire
Copper Clad Aluminum (Cu/Al)
Conductivity: 65% IACS
Diameter: Width: 0.1mm-5mm, Thickness: 0.05mm-1mm
🏭
Copper Clad Aluminum Stranded Wire
Copper Clad Aluminum (Cu/Al)
Conductivity: 65% IACS
Diameter: 0.5mm - 50mm
🏭
Copper Flat Wire
Electrolytic Copper (Cu)
Conductivity: 101% IACS
Diameter: Width: 0.5mm - 20mm, Thickness: 0.1mm - 5mm
Title
Description
Image Caption