Manufacturing Process
This product is manufactured using Clad & Weld process with metallurgical bonding. It is NOT electroplated.
Metallurgical bonding creates a permanent atomic-level connection, ensuring superior reliability compared to electroplating. This enables excellent weldability, resistance to peeling during bending, and stable performance under thermal cycling conditions.
aluminum
Aluminum Flat Wire
High precision aluminum flat wire suitable for motor windings, transformers, inductors and lightweight electrical equipment.
Material
Pure Aluminum (Al)
Conductivity
61% IACS
Tensile Strength
110 MPa
Diameter
Width: 0.5mm - 20mm, Thickness: 0.1mm - 5mm
Applications
Motor Windings Transformers Inductors Lightweight Equipment
Detailed Specs
| Specification | Value |
|---|---|
| Purity | ≥99.6% |
| Standards | ASTM B231, GB/T 3195 |
| Temper | Soft, Hard, Half-Hard |
| Surface Quality | Burr-free, Oxidation-free |
Frequently Asked Questions
Related Products
Aluminum Strip
Pure Aluminum (Al)
Conductivity: 61% IACS
Diameter: Width: 5mm - 500mm, Thickness: 0.05mm - 3mm
Aluminum Foil
Pure Aluminum (Al)
Conductivity: 61% IACS
Diameter: Thickness: 0.006mm - 0.2mm
Aluminum Ribbon Wire
Pure Aluminum (Al)
Conductivity: 61% IACS
Diameter: Width: 0.1mm - 2mm, Thickness: 0.03mm - 0.5mm
Copper Flat Wire
Electrolytic Copper (Cu)
Conductivity: 101% IACS
Diameter: Width: 0.5mm - 20mm, Thickness: 0.1mm - 5mm
Copper Clad Aluminum Flat Wire
Copper Clad Aluminum (Cu/Al)
Conductivity: 65% IACS
Diameter: Width: 0.5mm-25mm, Thickness: 0.1mm-5mm
Nickel Clad Copper Flat Wire
Nickel Clad Copper (Ni/Cu)
Conductivity: 90% IACS
Diameter: Width: 0.5mm-20mm, Thickness: 0.1mm-3mm